高强度船体结构钢力学性能与化学成份:
钢材级别
|
屈服点σs
(MPa)不小于
|
抗拉强度σb(MPa)
|
伸长率σ%
不小于
|
碳
C
|
锰
Mn
|
硅
Si
|
硫
S
|
磷
P
|
A32
|
315
|
440-570
|
22
|
≤0.18
|
≥0.9-1.60
|
≤0.50
|
≤0.035
|
≤0.035
|
D32
|
|
|
|
|
|
|
|
|
E32
|
|
|
|
|
|
|
|
|
F32
|
≤0.16
|
≤0.025
|
≤0.025
|
|
|
|
|
|
A36
|
355
|
490-630
|
21
|
≤0.18
|
≤0.035
|
≤0.035
|
|
|
D36
|
|
|
|
|
|
|
|
|
E36
|
|
|
|
|
|
|
|
|
F36
|
≤0.16
|
≤0.025
|
≤0.025
|
|
|
|
|
|
A40
|
390
|
510-660
|
20
|
≤0.18
|
≤0.035
|
≤0.035
|
|
|
D40
|
|
|
|
|
|
|
|
|
E40
|
|
|
|
|
|
|
|
|
F40
|
≤0.16
|
≤0.025
|
≤0.025
|
|
|
|
|
|
中国船级社规范标准的一般强度结构钢分为:A、B、D、E四个质量等级(即CCSA、CCSB、 CCSD、CCSE);中国船级社规范标准的高强度结构钢为三个强度级别、四个质量等级。